ASTM A210 BOILER BAJA KARBON MEDIUM MULUS DAN TABUNG SUPERHEATER
| Model No. : | BT06 |
|---|---|
| status : | New |
Deskripsi Produk
ASTM A210 —American Society for Testing and Material Standards
ASME SA210 - AmericanSociety of Mechanical Engineers standar
Tujuan:
Untuk pipa boiler dan pipa buang boiler, termasuk sisi keamanan, kubah dan tabung penyangga dan tabung superheater ketebalan dinding minimum pipa baja karbon seamless.
Nilai baja produksi utama:
A-1, C, dll. Tidak dinegosiasikan, tetapi juga memasok baja dengan kualitas lain.
Peralatan mekanis:
| Standard | Grade | Tensile strength (MPa) | Yield strength (MPa) | Elongation (%) |
|
ASTMA210 ASME SA210 |
A-1 | ≥415 | ≥255 | ≥30 |
| C | ≥485 | ≥275 | ≥30 |
Komposisi kimia:
| Standard | Grade | Chemical Composition | |||||||||
| C | Si | Mn | P | S | Cr | Mo | Cu | Ni | V | ||
|
ASTM A210 ASME SA210 |
C | ≤0.35 | ≥0.10 | 0.29～1.06 | ≤0.035 | ≤0.035 | / | / | / | / | / |
| A-1 | ≤0.27 | ≥0.10 | ≤0.93 | ≤ 0.035 | ≤0.035 | / | / | / | / | / | |
Tabung yang sudah jadi panas tidak perlu diberi perlakuan panas. Tabung jadi dingin harus diberi anil subkritis, anil penuh, atau perlakuan panas normalisasi setelah proses finishing dingin akhir.
Tabung harus memiliki kekerasan tidak melebihi berikut ini: 79 HRB atau 143 HRB untuk Grade A-1,89 HRB atau 179 HRB untuk Grade C.
Uji Listrik Hidrostatis atau Tidak Merusak —Setiap tabung harus terkena hidrostatis, atau,
alih-alih pengujian ini, pengujian listrik tidak rusak dapat digunakan jika ditentukan oleh pembeli
Selain penandaan yang ditentukan dalam Spesifikasi A 450 / A 450M, penandaan harus menunjukkan
apakah tabung sudah jadi panas atau sudah dingin.