Model No. :	TC-191
Brand Name :
CAS No. :	123-45-5
Other Names :	unsaturated polyester resin
MF :	C8H4O3.C4H10O3.C4H2O3
EINECS No. :	208-750-2
Type :	Synthetic Resin And Plastics
Brand Name :	thousands chemicals
Model Number :	TC-191, TC-191
Appearance :	Light yellow viscous liquid
Acid Value :	25-30mgKOH/g
viscosity,25℃ :	0.25-0.45Pa.s
solid content :	61-70%
Gel time ,25℃ :	9-17min
Barco hardness :	41
Heat distortion temperature :	70℃
Bending strength :	112MPa
Tensile strength :	60MPa
Place of Origin :	Jiangsu, China
Purity :	70%

lagi

2yrs

Wuxi, Jiangsu, China

Agen
Distributor / Grosir

Kunjungi toko

Pemasok Emas
Sertifikasi Platform
Sertifikasi SGS

Jiangyin Thousands Chemicals Co.

VISIT THE STORE

Deskripsi Produk

Resin poliester tak jenuh Cina untuk pipa serat kaca, resin belitan filamen

Deskripsi Resin Polyester Tidak Jenuh

TC191 Tujuan Umum Resin poliester fitur viskositas rendah, kekuatan mekanik yang baik dan keuletan tinggi, cocok untuk semua Jenis produk FRP layup tangan.

Resin poliester tak jenuh Cina untuk pipa serat kaca, resin belitan filamen

properti resin poliester tak jenuh

Item	Range	unit	Testing method
appearance	Light yellow viscous liquid	—	GB/T 8237.4.1.1
Acid value	25-30	mgKOH/g	GB/T 2895
Viscosity,25℃	0.25-0.45	Pa.s	GB/T 7193.1
Solid content	61-70	%	GB/T 7193.3
Gel time ,25℃	9-17	min	GB/T 7193-2008

Pengujian Waktu Gel: 50% Cyclohexanone Peroxide Paste: 4%, Promotor E1: 4%

Properti Bodi Pengecoran Resin Polyester Tidak Jenuh

Item	Unit	Measured value	Testing method
Barco hardness	——	41	GB 3854—83
Heat distortion temperature	℃	70	GB 1634—04
Bending strength	MPa	112	GB/T 2570—95
Tensile Strength	MPa	60	GB/T 2568—95
Elongation at break	%	3.5	GB/T 2568—95
Impact strength	KJ/m2	10.2	GB/T 2571—95

Catatan: 1. Metode Persiapan Tubuh Menurut GB8237-87

2. Sistem Curing: Hardener 55% MEKP: 2%, Promotor E1: 2% Sistem Post Cure: 60 ℃ × 2 H + 80 ℃ × 2 H

resin poliester tak jenuh FRP data tipikal

Item	Unit	Measured data	Testing method
Bending strength	MPa	365	GB/T1449—83
Tensile Strength	MPa	290	GB/T1447—83
Impact strength	KJ/m2	235	GB/T 1451—83

Catatan: 1. Metode Persiapan Tubuh Menurut GB8237-87

2. Sistem Pemecahan: Hardener 55% MEKP: 2%, Promotor E1: 2% Sistem Post Cure: 60 ℃ × 3H + 11 0 ℃ × 3H

Video

2yrs

Wuxi, Jiangsu, China

Agen
Distributor / Grosir

Kunjungi toko

Pemasok Emas
Sertifikasi Platform
Sertifikasi SGS

Kirim pertanyaan Anda ke pemasok ini

mengirimkan permintaan

Peringatan Produk

Berlangganan kata kunci yang Anda minati. Kami akan mengirimkan produk terbaru dan terpanas ke kotak masuk Anda. Jangan lewatkan informasi perdagangan apa pun.

Langganan

Ikuti kami:

Penggunaan situs web ini merupakan pengakuan dan penerimaan syarat & ketentuan kami.