Model No. : | ASTM A268 |
---|---|
Brand Name : | UNTUK KAYA |
Standard : | ASTM A268 |
Ningbo, Zhejiang, China
Deskripsi Produk
Deskripsi Produk
Standard | ASTM A268 |
Matrial | TP405, TP410, TP429, TP430, TP443, TP446-1, TP446-2, TP409 |
Size | OD: 4-230mm WT: 1-30mm Length: According to Customer's Requirement |
Manufacture |
Tubes are made by seamless process. At the manufacturer's option,, tubing may be furnished either hot finished or cold finished. |
Surface Condition | The finished tubes are free of scale., slight amount of oxidation is not considered as scale |
Test and Inspection | Tension Test, Flaring Test, Flange Test, Reverse Test, Hardness Test, Hydrostatic or Nondestructive Electric Test |
Heat treatment |
As a final treatment, tubes shall be reheated to a temperature of 1200℉(650℃) or higher and cooled (as appropriate for the grade) to meet the requirements of this specification. The martensitic grade UNS S41500 shall be reheated to a temperature of 950℉ (510℃) or higher and cooled as appropriate to meet the requirements of this specification. |
Grade
|
TP405
|
TP410
|
TP429
|
TP430
|
TP443
|
TP446-1
|
TP446-2
|
-
|
TP409
|
UNS
|
S40500
|
S41000
|
S42900
|
S43000
|
S44300
|
S44600
|
S40800
|
S40900
|
|
C, max
|
0.08
|
0.15
|
0.12
|
0.12
|
0.20
|
0.20
|
0.12
|
0.08
|
0.08
|
Mn, max
|
1.00
|
1.00
|
1.00
|
1.00
|
1.00
|
1.00
|
1.00
|
1.00
|
1.00
|
P, max
|
0.04
|
0.04
|
0.04
|
0.04
|
0.04
|
0.04
|
0.04
|
0.045
|
0.045
|
S, max
|
0.03
|
0.03
|
0.03
|
0.03
|
0.03
|
0.03
|
0.03
|
0.045
|
0.045
|
Si, max
|
1.00
|
1.00
|
1.00
|
1.00
|
1.00
|
1.00
|
1.00
|
1.00
|
1.00
|
Ni, max
|
0.05
|
-
|
-
|
-
|
0.75max
|
0.75max
|
0.50max
|
0.80max
|
0.50max
|
Cr
|
11.5-14.5
|
11.5-13.5
|
14.0-16.0
|
16.0-18.0
|
18.0-23.0
|
23.0-27.0
|
23.0-27.0
|
11.5-13.0
|
10.5-11.7
|
Mo
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
Al
|
0.10-0.30
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
Cu
|
-
|
-
|
-
|
-
|
0.90-1.25
|
-
|
-
|
-
|
-
|
N
|
-
|
-
|
-
|
-
|
-
|
0.25
|
0.25
|
12xC min
|
6xC
min
|
Ti
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
1.10max
|
0.75max
|
Acara Produksi
1. Inspeksi Bahan Baku Masuk
2. Pemisahan Bahan Baku untuk menghindari campuran tingkat baja
3. Pemanasan dan Pematahan Akhir untuk Menggambar Dingin
4. Cold Drawing dan Cold Rolling, pemeriksaan on line
5. Perlakuan Panas, + A, + SRA, + LC, + N, Q + T
6. Straightening-Cutting untuk Inspeksi Pengukuran panjang yang ditentukan
7. Pengujian Machanical di laboratorium sendiri dengan Kekuatan Tarik, Kekuatan Hasil, Elongasi, Kekerasan, Dampak, Mictrostruture dll
8. Pengepakan dan Stocking
100% dari tabung baja kami diperiksa secara dimensional
100% dari tabung baja kami secara visual diperiksa untuk memastikan mereka memiliki kondisi permukaan yang sempurna dan tidak ada cacat permukaan.
100% uji arus pusar dan uji ultrosonik untuk menghilangkan cacat longitudinal dan transversal.
FAQ
T: Apakah Anda perusahaan atau pabrikan dagang?
A: Penemu, penyedia dan penyedia solusi pipa baja profesional
Q: Berapa lama waktu pengiriman Anda?
A: Umumnya adalah 7-14 hari jika barang dalam persediaan. atau 30-60 hari jika barang tidak dalam persediaan, itu sesuai dengan kuantitas.
Q: Apakah Anda menyediakan contoh tabung baja karbon mulus? apakah gratis atau ekstra?
A: Ya, kami dapat menawarkan sampel untuk biaya gratis tetapi perlu membayar biaya pengiriman.
Q: Apa syarat pembayaran Anda?
A: Pembayaran <= 1000USD, 100% di muka. Pembayaran> = 1000USD, 30% T / T di muka, saldo sebelum shippment.
Jika Anda memiliki pertanyaan lain, pls jangan ragu untuk menghubungi kami
TORICH ASTM A268 TP405 TP410 Seamless Ferritic dan Martenstic Stainless Steel Tube
Ningbo, Zhejiang, China
Kirim pertanyaan Anda ke pemasok ini