1 / 5
Brand Name : | CHUNHUAN |
---|---|
Tensile Strength : | (81~130)MPa |
Zhenjiang, Jiangsu, China
Deskripsi Produk
Tabung ekstrusi MENGINTIP
Tabung MENGINTIP diproduksi dengan proses kontinyu memecahkan masalah ketinggian dan lubang Shrinkage di dalam, yang juga dapat mengurangi biaya selama proses CNC. Hal ini banyak digunakan untuk pembuatan cincin penyegel, ring piston, memakai bush dan kursi nilai dalam minyak & gas, industri semikonduktor. Kami diekstrusi pipa MENGINTIP larget di Cina (OD590mm)
NO |
Dimension(mm) |
Weight(g) |
Notes |
1 |
Θ1.6*θ0.13*1000 |
2.6 |
Unit(m) |
2 |
Θ1.6*θ0.25*1000 |
2.5 |
Unit(m) |
3 |
Θ1.6*θ0.5*1000 |
2.4 |
Unit(m) |
4 |
Θ1.6*θ0.75*1000 |
2.0 |
Unit(m) |
5 |
Θ1.6*θ1.0*1000 |
1.6 |
Unit(m) |
6 |
Θ2.33*θ1.6*1000 |
2.9 |
Unit(m) |
7 |
Θ2.8*θ2.5*1000 |
1.6 |
Unit(m) |
8 |
Θ3.0*θ2.67*1000 |
1.9 |
Unit(m) |
9 |
Θ3.2*θ1.0*1000 |
9.4 |
Unit(m) |
10 |
Θ3.2*θ1.6*1000 |
7.8 |
Unit(m) |
11 |
Θ5.0*θ2.5*1000 |
19.1 |
Squeeze |
12 |
Θ5.0*θ4.5*1000 |
5.8 |
Squeeze |
13 |
Θ7.5*θ4.0*1000 |
42.6 |
Squeeze |
14 |
Θ10.2*θ8.0*1000 |
40.9 |
Squeeze |
15 |
Θ12.0*θ4.0*1000 |
81.6 |
Squeeze |
16 |
Θ12.45*θ8.88*1000 |
77.7 |
Squeeze |
17 |
Θ29.0*θ18.0*1000 |
527.6 |
Squeeze |
18 |
Θ39.0*θ31.0*1000 |
571.5 |
Squeeze |
19 |
Θ80.0*θ30.0*1000 |
5612.8 |
Squeeze |
20 |
Θ90.0*θ40.0*1000 |
6633.3 |
Squeeze |
21 |
Θ100.0*θ50.0*1000 |
7653.8 |
Squeeze |
22 |
Θ110.0*θ60.0*1000 |
8674.3 |
Squeeze |
23 |
Θ130.0*θ60.0*1000 |
13572.7 |
Squeeze |
24 |
Θ140.0*θ80.0*1000 |
13470.6 |
Squeeze |
25 |
Θ160.0*θ90.0*1000 |
17858.8 |
Squeeze |
26 |
Θ168.0*θ132.0*1000 |
11021.0 |
Squeeze |
27 |
Θ180.0*θ110.0*1000 |
20716.2 |
Squeeze |
28 |
Θ190.0*θ130.0*1000 |
19593.6 |
Squeeze |
29 |
Θ190.0*θ140.0*1000 |
16838.3 |
Squeeze |
30 |
Θ200.0*θ130.0*1000 |
23573.6 |
Squeeze |
31 |
Θ220.0*θ150.0*1000 |
26431.0 |
Squeeze |
32 |
Θ240.0*θ170.0*1000 |
29288.4 |
Squeeze |
33 |
Θ257.0*θ230.0*1000 |
13418.6 |
Squeeze |
34 |
Θ250.0*θ190.0*1000 |
26941.0 |
Squeeze |
35 |
Θ260.0*θ210.0*1000 |
23981.8 |
Squeeze |
36 |
Θ280.0*θ210.0*1000 |
35003.2 |
Squeeze |
37 |
Θ280.0*θ230.0*1000 |
26022.0 |
Squeeze |
38 |
Θ300.0*θ250.0*1000 |
28063.8 |
Squeeze |
39 |
Θ320.0*θ300.0*1000 |
12654.2 |
Squeeze |
40 |
Θ340.0*θ250.0*1000 |
54188.6 |
Squeeze |
41 |
Θ360.0*θ280.0*1000 |
52249.6 |
Squeeze |
42 |
Θ580.0*θ450.0*1000 |
136645.0 |
Squeeze |
MENGINTIP bahan kelas utama dan sifat khas
Item |
Test Standard |
Unit |
PEEK450G |
PEEK450GL30 |
PEEK450CA30 |
PEEK450FC30 |
100%PEEK |
PEEK+30%Glass fiber |
PEEK+30% Carbon fiber |
PEEK+30% (Carbon fiber+Graphite+PTFE) |
|||
Color |
|
|
Natural or Black |
Natural or Black |
Black |
Black |
Density |
ISO1183 |
g/cm3 |
1.3±0.01 |
1.5±0.01 |
1.4±0.01 |
1.43±0.01 |
Water Abs(25℃,24Hrs) |
ISO 62 |
% |
0.5 |
0.11 |
0.06 |
0.06 |
Mould shrinking percentage |
3mm,170℃ Flow direction |
% |
1.2 |
0.4 |
0.1 |
0.3 |
Perpendicular to flow direction |
% |
1.5 |
0.8 |
0.5 |
0.5 |
|
Melting point |
DSC |
℃ |
343 |
343 |
343 |
343 |
Distortion temperature |
ASTM D648 |
℃ |
163 |
315 |
315 |
293 |
Continuous using temperature |
UL 74685 |
℃ |
260 |
260 |
260 |
260 |
Coefficient of thermal expansion |
ASTM D 696 |
10-5℃ |
2.2 |
1.5 |
2.2 |
4.7 |
Tensile strength(23℃) |
ISO527-2/1B/50 |
Mpa |
100 |
155 |
220 |
134 |
Tensile elongation(23℃) |
ISO527-2/1B/50 |
% |
34 |
2 |
1.8 |
2.2 |
Bending strength(23℃) |
ISO 178 |
Mpa |
163 |
212 |
298 |
186 |
Compressive strength(23℃) |
ASTM D695 |
Mpa |
118 |
215 |
240 |
150 |
Lzop impact strength(no gap) |
ISO 180/U |
KJ/m2 |
No break |
51 |
46 |
32 |
Rockwell hardness |
ASTM D785 |
|
103 |
107 |
102 |
99 |
Flammable level |
UL 94 |
V-0@mm |
1.5 |
1.5 |
1.5 |
0.75 |
Dielectric strength |
IEC 248 |
KM/mm |
18 |
19 |
|
|
Dielectric constant |
IEC 250 |
|
3.2 |
3.2 |
|
|
Surface resistivity |
|
Ω |
1015 |
1015 |
3*106 |
5*106 |
Friction coefficient |
|
µ |
0.30-0.38 |
0.38-0.46 |
0.28 |
0.18 |
Zhenjiang, Jiangsu, China
Kirim pertanyaan Anda ke pemasok ini